Loading...
The URL can be used to link to this page
Your browser does not support the video tag.
Home
My WebLink
About
Type 410 - 420 Stainless Steel
Data are typical, are provided for informational purposes, and should not be construed as maximum or minimum values for specification or for final design, or for a particular use or application. The data may be revised anytime without notice. We make no representation or warranty as to its accuracy and assume no duty to update. Actual data on any particular product or material may vary from those shown herein. TM is trademark of and ® is registered trademark of ATI Properties, Inc. or its affiliated companies. ® The starburst logo is a registered trademark of ATI Properties, Inc. © 2014 ATI. All rights reserved. VERSION 1 (2/18/2014): PAGE 1 of 6 Allegheny Technologies Incorporated 1000 Six PPG Place Pittsburgh, PA 15222-5479 U.S.A. www.ATImetals.com Technical Data Sheet ATI 410™/ATI 420™/ATI 425 Mod™/ ATI 440A™/ATI 440C™ ATI 410™/ATI 420™/ATI 425 Mod™/ATI 440A™/ATI 440C™ Stainless Steel: Martensitic (UNS S41000/S42000/xxxxx/S44002/S44004) GENERAL PROPERTIES ATI 410, ATI 420, ATI 425 Modified, and ATI 440A alloys (see composition on Page 2) are hardenable, straight-chromium stainless steels which combine superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless steels. Oil quenching these alloys from temperatures between 1800°F to 1950°F (982-1066°C) produces the highest strength and/or wear resistance as well as corrosion resistance. A range of as-quenched hardness is achieved in these alloys by varying the carbon level from 0.15% maximum in Type 410 alloy to 0.60-0.75% in ATI 440A alloy. These alloys are used where strength, hardness, and/or wear resistance must be combined with corrosion resistance. APPLICATIONS A major use for these grades of heat treatable stainless steels is in cutlery. Depending on the customer's end-use requirements, cutlery alloys are usually selected with respect to heat treating response, mechanical properties and fabricating characteristics. When sufficient amounts of carbon are added to straight chromium stainless steels, the alloy then has the capability to transform its microstructure through proper heat treatment (hardening) into one that will possess optimum strength, hardness, edge retention, and wear resistance. The presence of sufficient chromium will impart the necessary corrosion resistance and form chromium carbide particles that enhance the wear resistance of the given alloy. The higher the carbon content, the greater the amount of chromium carbide particles, and the greater the strength and hardness for heat treatable straight-chromium stainless steels. When blanking cutlery parts from annealed raw material stock, ATI 410, ATI 420 alloys and their higher carbon versions (ATI 410HC and ATI 420HC) will usually exhibit hardness, yield strength, and tensile strength that are low enough for fine blanking purposes. However, ATI 440A alloy is not readily amenable to fine blanking due to its higher strength and hardness in the annealed condition; and therefore, could require more powerful presses to blank parts. In addition, the presence of large primary carbides in ATI 440A alloy would tend to reduce die life. When buffing blanked parts, the higher hardness of ATI 440A alloy in the heat treated condition (hardened) would mean less residual buffing lines on the surfaces of parts but the large primary carbides could be dislodged during buffing which would produce scratches called “comet-tails”. Stainless steels lower in carbon content are essentially free of "comet-tails". Other applications for these grades include dental and surgical instruments, nozzles, valve parts, hardened steel balls and seats for oil well pumps, separating screens and strainers, springs, shears, and wear surfaces. PRODUCT FORMS These alloys are available as plate, sheet, strip and flat bars. Data are typical, are provided for informational purposes, and should not be construed as maximum or minimum values for specification or for final design, or for a particular use or application. The data may be revised anytime without notice. We make no representation or warranty as to its accuracy and assume no duty to update. Actual data on any particular product or material may vary from those shown herein. TM is trademark of and ® is registered trademark of ATI Properties, Inc. or its affiliated companies. ® The starburst logo is a registered trademark of ATI Properties, Inc. © 2014 ATI. All rights reserved. VERSION 1 (2/18/2014): PAGE 2 of 6 Allegheny Technologies Incorporated 1000 Six PPG Place Pittsburgh, PA 15222-5479 U.S.A. www.ATImetals.com Technical Data Sheet ATI 410™/ATI 420™/ATI 425 Mod™/ ATI 440A™/ATI 440C™ CHEMICAL COMPOSITION Stainless Steels Element in Weight Percent Carbon Manganese Silicon Chrom ium Molybdenum Nickel Sulfur Phosphorus ATI 410* 0.08-0.15 1.00 m ax 1.00 m ax 11.5-13.5 --- 0.75 max 0.030 max 0.040 max ATI 420** 0.15-0.40 1.00 max 1.00 max 12.0-14.0 --- 0.75 max 0.030 max 0.040 max ATI 425 Mod 0.50-0.55 1.00 max 1.00 max 13.0-14.0 0.80-1.20 0.50 max 0.030 max 0.040 max ATI 440A 0.60-0.75 1.00 max 1.00 max 16.0-18.0 0.75 max --- 0.030 max 0.040 max ATI 440C 0.95-1.20 1.00 max 1.00 max 16.0-18.0 0.75 max --- 0.030 max 0.040 max *A higher carbon version of ATI 410 alloy is also available called ATI 410HC (nominal 0.21% C) alloy. **A higher carbon version of ATI 420 alloy is also available called ATI 420HC (nominal 0.44% C) alloy. MECHANICAL PROPERTIES Typical compositions, annealed mechanical properties and hardening response for the various ATI martensitic stainless steels are presented below. Stainless Steels Typical Composition (Weight Percent) T ypical Annealed Properties Hardening Response C Cr Mo HRB 0.2% Offset Yield Strength Ksi (MPa) Tensil e Stre ngth Ksi (MPa) Elongation, Percent in 2" (51 mm) HRC ATI 440A 0.64 16.5 -- 95 62 (427) 104 (717) 20 57-60 ATI 425 Mod 0.55 13.5 1.0 93 55 (379) 94 (648) 24 57-60 89* 45 (310) 86* (593) 25* ATI 420HC** 0.44 13.0 -- 88 45 (310) 87 (600) 28 56-59 ATI 420 0.38 13.0 -- 87 45 (310) 85 (586) 29 53-57 ATI 410HC** 0.21 12.5 -- 83 43 (31 0) 78 (538) 30 45-52 ATI 410 0.14 12.5 -- 82 42 (290) 74 (510) 34 38-45 * Fine blanking quality **HC means higher carbon version of standard grade Data shown below give typical mechanical properties of martensitic stainless steels obtained with various drawing temperatures after austenitizing at 1800-1950°F (982-1066°C) followed by an oil quench and a two hour temper. Heat-to-heat variations can be anticipated. Modulus of Elasticity 29 x 106 psi (200 GPa) Data are typical, are provided for informational purposes, and should not be construed as maximum or minimum values for specification or for final design, or for a particular use or application. The data may be revised anytime without notice. We make no representation or warranty as to its accuracy and assume no duty to update. Actual data on any particular product or material may vary from those shown herein. TM is trademark of and ® is registered trademark of ATI Properties, Inc. or its affiliated companies. ® The starburst logo is a registered trademark of ATI Properties, Inc. © 2014 ATI. All rights reserved. VERSION 1 (2/18/2014): PAGE 3 of 6 Allegheny Technologies Incorporated 1000 Six PPG Place Pittsburgh, PA 15222-5479 U.S.A. www.ATImetals.com Technical Data Sheet ATI 410™/ATI 420™/ATI 425 Mod™/ ATI 440A™/ATI 440C™ Typical Mechanical Properties of Heat Treated Martensitic Stainless Steels Heat Treatment ATI 410™ (0.14 %C) Hardened 1800°F (982°C) ATI 420™ (0.25 %C) Hardened 1900°F (1038°C) ATI 425™ (0.55 %C) Hardened 1900°F (1038°C) ATI 440A™ (0.62 %C) Hardened 1900°F (1038°C) Rockwell Hardness 0.2 YS, Ksi (MPa) UTS, Ksi (MPa) Rockwell Hardness 0.2 YS, Ksi (MPa) UTS, Ksi (MPa) Rockwell Hardness 0.2 YS, Ksi (MPa) UTS, Ksi (MPa) Rockwell Hardness 0.2 YS, Ksi (MPa) UTS, Ksi (MPa) Annealed* 81 HRB 45.4 (313) 80.4 (554) 85 HRB 51.5 (355) 85.8 (592) 90 HRB 57.4 (396) 86.3 (595) 94 HRB 51.6 (354) 108.4 (747) Hardened+ Tempered 400°F (204°C) 43 HRC 156.1 (1076) 202.9 (1399) 48 HRC 190.1 (1311) 255.2 (1759) 53 HRC 200.9 (1385) 270.9 (1868) 54 HRC 229.0 (1579) 293.3 (2022) Hardened+ Tempered 550°F (288°C) 40 HRC 148.3 (1022) 187.0 (1289) 44 HRC 176.0 (1213) 229.6 (1583) 50 HRC 197.2 (1360) 250.8 (1729) 50 HRC 220.2 (1518) 272.6 (1879) Hardened+ Tempered 600°F (316°C) 40 HRC 148.8 (1026) 186.1 (1283) 45 HRC 179.0 (1234) 232.9 (1606) 53 HRC 196.0 (1351) 245.1 (1690) 53 HRC 222.0 (1531) 273.2 (1883) Hardened+ Tempered 800°F (427°C) 41 HRC 132.9 (916) 188.5 (1300) 46 HRC 185.6 (1280) 236.0 (1627) 53 HRC 210.6 (1452) 255.1 (1759) 53 HRC 233.6 (1610) 272.8 (1881) Hardened+ Tempered 900°F (482°C) 41 HRC 122.6 (845) 188.3 (1298) 46 HRC 179.3 (1236) 233.0 (1606) 52 HRC 198.4 (1368) 234.8 (1619) 52 HRC 212.6 (1466) 269.5 (1858) Hardened+ Tempered 1000°F (538°C) 35 HRC 127.9 (882) 154.3 (1063) 36 HRC 137.9 (951) 158.5 (1093) 43 HRC 176.6 (1218) 208.0 (1434) 41 HRC 147.0 (1013) 177.5 (1224) Hardened+ Tempered 1200°F (649°C) 98 HRB 85.5 (589) 111.2 (767) 23 HRC 94.6 (652) 121.6 (838) 29 HRC 107.8 (743) 135.7 (936) 31 HRC 105.5 (727) 135.4 (933) *See Heat Treatment section for annealing information For maximum hardness and strength, a hardening heat treatment is necessary. The stainless steel alloys shown in the table above were heated as sheet samples for 60 minutes per inch of thickness at 1800°F (982°C) for Type ATI 410 and at 1900°F (1038°C) for ATI 420, ATI 425 Modified, and ATI 440A alloys, and then air cooled to room temperature. The as-quenched structure of fresh martensite must be tempered to restore some ductility. The samples depicted in the table were tempered at temperatures from 400°F (204°C) to 1200°F (649°C) for two hours; note that their hardnesses and strengths changed very little with increases in tempering temperature up to 900°F (482°C). Data are typical, are provided for informational purposes, and should not be construed as maximum or minimum values for specification or for final design, or for a particular use or application. The data may be revised anytime without notice. We make no representation or warranty as to its accuracy and assume no duty to update. Actual data on any particular product or material may vary from those shown herein. TM is trademark of and ® is registered trademark of ATI Properties, Inc. or its affiliated companies. ® The starburst logo is a registered trademark of ATI Properties, Inc. © 2014 ATI. All rights reserved. VERSION 1 (2/18/2014): PAGE 4 of 6 Allegheny Technologies Incorporated 1000 Six PPG Place Pittsburgh, PA 15222-5479 U.S.A. www.ATImetals.com Technical Data Sheet ATI 410™/ATI 420™/ATI 425 Mod™/ ATI 440A™/ATI 440C™ PHYSICAL PROPERTIES The values reported below are typical for the alloys in the annealed condition. Property ATI 410™ ATI 420™ ATI 425 Mod™ ATI 440A™ Specific Gravity Density Lbs / in3 7.75 0.280 7.73 0.278 7.72 0.278 7.74 0.279 Specific Heat Btu/lb. • °F T hermal Conductivity at 212°F (100°C) Btu/(hr • ft •°F) W /m•K 0.11 14.4 24.9 0.11 14.0 24.2 0.11 14.0 24.2 0.11 14.0 24.2 Electrical Resistivity Microhm-cm 68°F (20°C) 56 56 61 62 Coefficient of Thermal Expansion 68 - 392°F, in/in°F 20-200°C, cm/cm/°C 68-1112°F, in/in/°F 20-600°C, cm/cm/°C 6.0 x 10-6 10.8 x 10-6 7.0 x 10-6 12.5 x 10-6 6.0 x 10-6 10.8 x 10-6 7.0 x 10-6 12.5 x 10-6 6.2 x 10-6 11.2 x 10-6 7.1 x 10-6 12.8 x 10-6 6.0 x 10-6 10.8 x 10-6 6.8 x 10-6 12.2 x 10-6 Melting Range 2700-2790°F 1482-1532°C 2650-2750°F 1454-1510°C 2600-2750°F 1427-1510°C 2550-2750°F 1399-1510°C CORROSION RESISTANCE ATI 410, ATI 420, ATI 425 Mod, and ATI 440A alloys exhibit good corrosion resistance to atmospheric corrosion, potable water, and to mildly corrosive chemical environments because of their ability to form a tightly adherent oxide film which protects their surfaces from further attack. Their exposure to chlorides in everyday type activities (e.g., food preparation, sport activities...) is generally satisfactory when proper cleaning is performed after exposure to use. See additional comments on corrosion properties under the section “Surface Preparation”. General Corrosion Behavior Compared With Other Nonaustenitic Stainless Steels* 5% Test Solution at 120°F (49°C) Corrosion Rate in Mils per Year and Millimeters per Year (mm/a) ATI 409™ ATI 410™ ATI 420™ ATI 425 Mod™ ATI 440A™ ATI 430™ Acetic Acid 0.88 (0.022) 0.079 (0.002) 1.11 (0.028) 4.79 (0.122) 2.31 (0.0586) 0.025 (0.0006) Phosphoric Acid (0.059) (0.002) 0.062 (0.002) 0.068 (0.002) 0.593 (0.015) 0.350 (0.009) 0.029 (0.001) *Hardened martensitic grades were tested after tempering at 400°F (204°C). As shown in the above table, these alloys have good corrosion resistance to low concentrations of mild organic and mineral acids. Data are typical, are provided for informational purposes, and should not be construed as maximum or minimum values for specification or for final design, or for a particular use or application. The data may be revised anytime without notice. We make no representation or warranty as to its accuracy and assume no duty to update. Actual data on any particular product or material may vary from those shown herein. TM is trademark of and ® is registered trademark of ATI Properties, Inc. or its affiliated companies. ® The starburst logo is a registered trademark of ATI Properties, Inc. © 2014 ATI. All rights reserved. VERSION 1 (2/18/2014): PAGE 5 of 6 Allegheny Technologies Incorporated 1000 Six PPG Place Pittsburgh, PA 15222-5479 U.S.A. www.ATImetals.com Technical Data Sheet ATI 410™/ATI 420™/ATI 425 Mod™/ ATI 440A™/ATI 440C™ General Corrosion Behavior Compared With Other Nonaustenitic Stainless Steels* Test Solution at 75°F (24 °C), pH 5 Breakthrough Pitting Potential [Volts vs SCE] in Sodium Chloride Solution ATI 409™ ATI 4 10™ ATI 4 20™ ATI 425 Mod™ ATI 4 40A™ ATI 4 30™ 100 ppm Chloride 0.439 0.502 0.581 0.619 0.598 0.590 *Hardened Martensitic grades were tested after tempering at 400°F (204°C). Test samples had ground surfaces. Potentiodynamic anodic polarization measurements, as shown above, can be used to determine the relative resistance of a stainless steel to the initiation of localized chloride attack (pitting and crevice corrosion). With this technique the “breakdown potential” is measured, and is defined as the potential at which the anodic current increases rapidly due to initiation of localized attack. The more positive or noble the breakdown potential the more corrosion resistant the alloy. The above table presents the average break-down potential for the hardenable alloys as well as ATI 430 and ATI 409 alloys for comparison. The anodic polarization results show that alloys such as ATI 425 Mod, ATI 440A, and ATI 430 alloys with their higher chromium or combination of chromium and molybdenum contents are more resistant to localized chloride attack. FABRICATING PROPERTIES Machining These alloys should be machined in the annealed condition using surface speeds of 60 to 80 feet (18.3-24.4 m) per minute. Surface Preparation For maximum corrosion resistance to chemical environments, it is essential that the stainless steel surface be free of all heat tint or oxide formed during forging, annealing, or heat treating. All surfaces must be ground or polished to remove any traces of oxide and surface decarburization. The parts should then be immersed in a warm solution of 10-20% nitric acid to remove any residual iron. A thorough water rinse should follow the nitric acid treatment. Structure In the annealed condition, ATI 410, ATI 420, ATI 425 Mod, and ATI 440A alloys consist of ferrite and carbides. Higher carbon and higher chromium material such as ATI 440A alloys in the annealed condition will also contain large scattered primary carbides. When these alloys are heat treated at high temperatures [1800°F-1950°F (982-1066°C)] austenite will form and transform to martensite upon cooling to room temperature (i.e., air cool or oil quench). The hardness of the martensite will increase with increasing carbon content to a point where the martensite becomes saturated with carbon, hence ATI 440A alloys will exhibit a higher as-quenched hardness than ATI 410 alloys. Carbon also combines with carbide formers such as chromium to form chromium carbides which are dispersed throughout the micro-structure to provide added wear resistance, as does higher hardness. Forging The suggested initial forging temperature range for ATI 410, ATI 420 and ATI 425 Mod alloys is 2000-2200°F (1093-1204°C) and 1900-2200°F (1038-1204°C) for ATI 440A alloy. Forging or hot working should always be followed by annealing to avoid stress cracking. HEAT TREATMENT To anneal these alloys, heat to 1550°F-1650°F (843-899°C) for ATI 420, ATI 425 Mod, and ATI 440A alloys or 1500°F-1550°F (815-842°C) for ATI 410 alloy and hold for one hour per inch of thickness and furnace cool to room temperature. Such annealing should produce a Brinell hardness of 126-192 HB in ATI 410 material. The higher carbon alloys, ATI 420, ATI 425 Mod, and ATI 440A alloys, will have somewhat higher hardness values. A hardening heat treatment is necessary to bring out the maximum hardness and wear resistance. Since these materials absorb heat very slowly, they should be heated gradually and allowed to remain at temperature long enough to ensure uniform temperature in thick sections. For maximum strength, hardness, and corrosion resistance, slowly heat the alloy to 1800°F (982°C) for ATI 410 alloy and to 1850°F-1950°F (1010-1066°C) for ATI 420, ATI 425 Mod, and ATI 440A alloys and quench to room temperature in oil. For thin sections, air cooling can be substituted for the oil quench. If retained austenite is known to be present Data are typical, are provided for informational purposes, and should not be construed as maximum or minimum values for specification or for final design, or for a particular use or application. The data may be revised anytime without notice. We make no representation or warranty as to its accuracy and assume no duty to update. Actual data on any particular product or material may vary from those shown herein. TM is trademark of and ® is registered trademark of ATI Properties, Inc. or its affiliated companies. ® The starburst logo is a registered trademark of ATI Properties, Inc. © 2014 ATI. All rights reserved. VERSION 1 (2/18/2014): PAGE 6 of 6 Allegheny Technologies Incorporated 1000 Six PPG Place Pittsburgh, PA 15222-5479 U.S.A. www.ATImetals.com Technical Data Sheet ATI 410™/ATI 420™/ATI 425 Mod™/ ATI 440A™/ATI 440C™ after the austenitizing and quench to room temperature, additional hardening response may be achieved by sub-zero cooling to about -100°F (-73°C). The as-quenched structure of fresh martensite is quite brittle and should be stress-relieved or tempered at approximately 400°F to 500°F (204-260°C) to restore some ductility. During tempering between approximately 300°F (149°C) and 600°F (316°C), a relaxation of the martensite structure occurs whereby the volumetric stresses associated with the formation of martensite upon quenching are relieved. As a result, the martensite still exhibits its high hardness and wear resistance properties but some ductility is introduced at the loss of a few points of hardness.